A comparative study on mechanical properties of fully dense 420 stainless steel parts produced by modified binder jet printing

Shin Department of Biosystems Engineering, Chungbuk National University, ChungBuk, Cheongju, South Korea|
Patrick (7005012457) | Haseung (57926912600); Kwon | Se-Hyun (17346024800); Chung | Tae-Yeong (57546998200); Ko College of Engineering and Computer Science, VinUniversity, Hanoi, Viet Nam| Dohoon (57546613000); So Department of Mechanical Engineering, Michigan State University, East Lansing, MI, United States| Truong (56400339600); Lee Korea Institute of Industrial Technology Incheon, South Korea| Chang-Seop (57190805170); Do Department of Mechanical Engineering, Vinh University, Hanoi, Viet Nam|

Materials and Design Số , năm 2022 (Tập 224, trang -)

ISSN: 2641275

ISSN: 2641275

DOI: 10.1016/j.matdes.2022.111343

Tài liệu thuộc danh mục:

Article

English

Từ khóa: Cold rolling; Density (specific gravity); Fatigue of materials; Metal cladding; Stainless steel; Steel sheet; Binder jet printing; Comparatives studies; Fatigue strength; Jet printing; Modified binders; New protocol; Sintering condition; Static strength; Steel parts; Traditional manufacturing; Sintering
Tóm tắt tiếng anh
The mechanical properties of the parts produced by binder jet printing (BJP) are often considerably inferior to those of the parts produced by traditional manufacturing processes because BJP parts retain at best about 95% of theoretical density after full sintering. To address this deficiency of BJP, a new processing protocol was developed, which enables us to produce fully dense parts under an isothermal sintering condition. This paper compares the mechanical properties of the stainless steel 420 (SS420) parts produced by the several variations of this new protocol against commercially available cold rolled SS420 parts with and without the heat-treatment under the similar sintering condition used in the new protocol. The mechanical properties examined include elastic modulus and both static and fatigue strengths. The only minor drawback of the new protocol is the dimensional shrinkage occurring during sintering. However, this can be easily compensated by printing the part geometry about 15% larger in the linear dimension with the starting powder used in this study. The final results showed the excellent static and fatigue strengths of the SS420 specimens produced with the new BJP protocol, implicating the potential structural applications of the BJP parts. � 2022 The Author(s)